Objective To investigate the effect of homograft of marrow mesenchymal stem cells (MSCs) seeded onto poly-L-lactic acid (PLLA)/gelatin on repair of articular cartilage defects. Methods The MSCs derived from36 Qingzilan rabbits, aging 4 to 6 months and weighed 2.5-3.5 kg were cultured in vitroand seeded onto PLLA/gelatin. The MSCs/ PLLA/gelatin composite was cultured and transplanted into full thickness defects on intercondylar fossa. Thirty-six healthy Qingzilan rabbits were made models of cartilage defects in the intercondylar fossa. These rabbits were divided into 3 groups according to the repair materials with 12 in each group: group A, MSCs and PLLA/gelatin complex(MSCs/ PLLA/gelatin); group B, only PLLA/gelatin; and group C, nothing. At 4,8 and 12 weeks after operation, the gross, histological and immunohistochemical observations were made, and grading scales were evaluated. Results At 12 weeks after transplantation, defect was repaired and the structures of the cartilage surface and normal cartilage was in integrity. The defects in group A were repaired by the hylinelike tissue and defects in groups B and C were repaired by the fibrous tissues. Immunohistochemical staining showed that cells in the zones of repaired tissues were larger in size, arranged columnedly, riched in collagen Ⅱ matrix and integrated satisfactorily with native adjacent cartilages and subchondral bones in group A at 12 weeks postoperatively. In gross score, group A(2.75±0.89) was significantly better than group B (4.88±1.25) and group C (7.38±1.18) 12 weeks afteroperation, showing significant differences (P＜0.05); in histological score, group A (3.88±1.36) was better than group B (8.38±1.06) and group C (13.13±1.96), and group B was better than group C, showing significant differences (P＜0.05). Conclusion Transplantation of mesenchymal stem cells seeded onto PLLA/gelatin is a promising way for the treatment of cartilage defects.
Objective To explore the methods of repairing cartilagedefects and to introduce the clinical experience with the autologous osteochondral transplantation. Methods Twenty-five patients with chondral and osteochondral defects of the weight-bearing surfaces were treated by the autologous osteochondral transplantation for the repair of the chondral and osteochondral defects of the unweightbearing surfaces under arthroscope. According to the shape of the defects, the different dimensions of the osteochondral autograft were selected. All the patients began the training of the continuous passive motion after operation. Six weeks after operation, the patients began to walk in the weightbearing habitus. However, in the control group, another 25 patients were retrospectively analyzed, who had chondral and osteochondral defects of the weight-bearing surfaces but were treated only by the cleaning and drilling procedures. The scores evaluated bythe Brittberg-Peterson scoring scale of the 2 group were 98.65±9.87 and 96.98±8.94 respectively. Results The follow-upfor 3-24 months after operation revealed that the treated knee joint had a goodmotion extent. The pain was obviously alleviated. Based on the longitudinal study with the three-dimensional spoiled magnetic resonance imaging (MRI), the signal intensity of the repaired tissues approached to the normal condition. The scores evaluated by the Brittberg-Peterson scoring scale were almost zero 3 monthsafter operation in the experimental group, and the scores were 58.48±6.98 inthe control group. There were significant differences between the experimental group and the control group(P＜0.01). Conclusion Autologous osteochondral transplanation under arthroscope is a good curative method for the cartilage defects, with advantages of minimal invasiveness and avoidanceofrejections resulting from allografts. However, its long-term effect needs to befurther studied. The conventional therapies including cleaning and drilling are useful in alleviating the symptoms.
Objective To investigate the clinical application of periosteal autograft in repair of cartilage defect caused by osteoarthritis of knee. Methods From 1996 to 1999, 36 knees of cartilage defect of knee joint in 28 cases were treated. In the operation, the cracked degenerative cartilage was removed before free periosteum from tibia was transplanted to repair the defect, and the meniscuses in 8 knees of the 36 knees were reconstructed. After operation, early continuous passive movement was adopted for 4 weeks, and 8 knees with reconstruction ofthe meniscus were immobilized by plaster splint for 7 days after operation and before passive movement. All of the cases were followed up for 1 to 4 years before clinical evaluation in symptoms, signs and radiological findings. Results The general satisfactory rate was 86.1%, in which the function was excellent in 22 knees and good in 9 knees. Conclusion The periosteal autograft is a good choice for repairing cartilage defect due to osteoarthritis, with a satisfactory outcomein the short term.
ccording to the characteristics of periosteum which have a copacity for regrowth of cartilage,free autogenous osteoperiosteal grafts taken from the medial side of the metaphsis of the tibia had beenused to reconstruct the osteochondral defects of the articular surface of the knee joint. The mothod wasillustrated by five cases which included of osteochondritis dissecans, subchondral osteonecrosis and oldfracture of the patella. By the period of 16-26 monthes follow up, using knee function...
Objective To investigate the feasibility of repairing thyroid cartilage defects by implantation of chondrocyte-allogenous acellular cartilaginousmatrix(chondrocyte-ACM) composite in rabbits. Methods The thyroid chondrocyteswere isolated and co-cultured in vitro with allogenous acellular cartilaginousmatrix(ACM) to form the chondrocyte-ACM composite. The composite was analyzed histologically and was used to repair defects of thyroid cartilage. Eighteen New Zealand adult rabbits were made the defect models of thyroid cartilage at the two sides and divided into three groups. The defects were repaired with chondrocyte-ACM composite in the experimental group(n=6), with simple ACM in the ACM group (n=6)and without any material in the control group(n=6). The animals were sacrificed at 8 weeks after operation. The specimens were evaluated histologically. Results In vitro, the growth of chondrocytes was observed on the surface of allogenous acellular cartilaginous matrix and no chondrocytes grew inside the matrix. The defect filled with muscle and connective tissues in control group; the lymphocyte infiltration was observed in the matrix and no new cartilage formationoccurred at 8 weeks after operation in simple ACM group and experimental group.So the defect repair of rabbits thyroid cartilage failed. Conclusion The allogenous acellular cartilaginous matrixfailed to serve as a scaffold for chondrocytes both in vitro and in vivo. The allogenous acellular cartilaginous matrixshould be improved.
The repair of defects of articular cartilage has continued to be a difficult problem. This article provided a collective review from literature pertaining to the advances gained in the repair of cartilaginous defects. In the spontaneous repair, if the defect of the cartilage was less than 3 mm, might result in complete or partial repair, but in those the diameter was more than 3 mm, the defect could not be repaired by normal cartilage. Although the cartilaginous autograft could give good result, but it could not be widely applied because short of supply of the autogenous cartilage. Cartilagious allograft could not be taken to repair cartilaginous defect because of reaction from tissue rejection. The transplantation of periosteal or perichondral graft had been tried but was eventually abandoned because of poor long-term result. The transplantation of free chondrocytes might be a method of hope. In general, transplantation of free chondrocytes into the cartilaginous defect will be lost. The supply of autogenous chondrocytes was very limited, and the heterogenous chondrocytes would inflict immunoreaction after being transplanted. In late of 1980, a new concept of tissue engineering was proposed. The problem that a scaffold of appropriate material which could hold the free chondrocytes in place from being lost might undergo proliferation and differentiation into new cartilage was far from being solved. Although tissue engineering still had various problems needed further investigation, but it will probably be the main direction of development in this field.
Objective To investigate the effect of allogeneic chondrocytes-calcium alginate gel composite under the intervention of low intensive pulsed ultrasound (LIPUS) for repairing rabbit articular cartilage defects. Methods Bilateral knee articular cartilage were harvested from 8 2-week-old New Zealand white rabbits to separate the chondrocytes by mechanical-collagen type II enzyme digestion. The 3rd passage chondrocytes were diluted by 1.2% sodium alginate to 5 × 106 cells/mL, then mixed with CaCl2 solution to prepare chondrocytes-calcium alginate gel composite, which was treated with LIPUS for 3 days (F0: 1 MHz; PRF: 1 kHz; Amp: 60 mW/cm2; Cycle: 50; Time: 20 minutes). An articular cartilage defect of 3 mm in diameter and 3 mm in thickness was established in both knees of 18 New Zealand white rabbits (aged 28-35 weeks; weighing, 2.1-2.8 kg), and divided into 3 groups randomly, 6 rabbits in each group: LIPUS group, common group, and model group. Defect was repaired with LIPUS-intervention gel composite, non LIPUS-intervention gel composite in LIPUS group and common group, respectively; defect was not treated in the model group. The general condition of rabbits was observed after operation. The repair effect was evaluated by gross and histological observations, immunohistochemical staining, and Wakitani score at 8 and 12 weeks after operation. Results Defect was filled with hyaline chondroid tissue and white chondroid tissue in LIPUS and common groups, respectively. LIPUS group was better than common group in the surface smooth degree and the degree of integration with surrounding tissue. Defect was repaired slowly, and the new tissue had poor elasticity in model group. Histological observation and Wakitani score showed that LIPUS group had better repair than common group at 8 and 12 weeks after operation; the repair effect of the 2 groups was significantly better than that of model group (P lt; 0.05); and significant differences in repair effect were found between at 8 and 12 weeks in LIPUS and common groups (P lt; 0.05). The collagen type II positive expression area and absorbance (A) value of LIPUS and common groups were significantly higher than those of model group (P lt; 0.05) at 8 and 12 weeks after operation, and the expression of LIPUS group was superior to that of common group at 12 weeks (P lt; 0.05); and significant differences were found between at 8 and 12 weeks in LIPUS group (P lt; 0.05), but no significant difference between 2 time points in common and model groups (P gt; 0.05). Conclusion Allogeneic chondrocytes-calcium alginate gel composite can effectively repair articular cartilage defect. The effect of LIPUS optimized allogeneic chondrocytes-calcium alginate gel composite is better.
Objective To evaluate the immunological reaction and the outcome of allogeneic chondrocyte transplantation in repairing articular cartilage defects in porcins. Methods Full articular cartilage from the knee of two Shanghai white porcins about one-month-old was removed and cut mechanically, digested by 0.25% trypsin and 0.2% type Ⅱ collagenase and cultured in 10％ DMEM medium. Defects of 0.5 cm×0.5 cm involving the subchodral bone were created in both the left and right femur condyloid in 8 two-month-old Yunnai bama porcins. Allogeneic chondrocyte transplantation were implanted in defects at a density of (1.0-2.0)×106,0.2 ml. The lymphocytes from the receivers’ blood were collected before transplantation and after 3, 5, 7 and 12 weeks of transplantation, then mixed with allogeneic chondrocytes to determin the lymphocyte stimulation index(SI) in vitro. The histological observation in vivo was made after 5, 7 and 24 weeks of transplantation. Results Lymphocyte SI at 3, 5, 7 and 12 weeks(1.457±0.062,1.739±0.142,1.548±0.047，1.216±0.028) after transplantation was higher than that before transplantation(1.102±0.034，Plt;0.05). SI began to increase in the 3rd week and reached the peak value in the 5th week, then gradually declined at the 7th and 12th weeks, showing significant differences when compared with in the 5th week (Plt;0.05). Inflammation and lymphocytes infiltration could be seen in subchondral bone and the intergration area between repair tissue and normal cartilage in the 5th week, and then decreased and limited in subchondral bone in the 7th week. Defects were filled with cartilage tissue, which had good intergration with subchondral bone at 24 weeks after transplantation. Conclusion Immunological reactions can be found at early stage of allogeneic chondrocyte transplantation and then decreased with the time, the fullthickness articular cartilage defects could be repaired mainlywith hyaline cartilage by the allogeneic chondrocyte transplantation. This may provide a new method to repair articular cartilage defects clinically.
Objective To study the biological characteristic and potential of chondrocytes grafting cultured on fascia in repairing large defect of articular cartilage in rabbits. Methods Chondrocytes of young rabbits were isolated and subcultured on fascia. The large defect of articular cartilage was repaired by grafts of freeze-preserved and fresh chondrocytes cultured on fascia, and free chondrocytes respectively; the biological characteristic and metabolism were evaluated bymacroscopic, histological and immunohistochemical observations, autoradiography method and the measurement of nitric oxide content 6, 12, 24 weeks after grafting. Results The chondrocytes cultured on fascia maintained normal growth feature and metabolism, and there was no damage to chondrocytes after cryopreservation; the repaired cartilage was similar to the normal cartilage in cellular morphology and biological characteristics. Conclusion Chondrocytes could be cultured normally on fascia, which could be used as an ideal carrier of chondrocytes.
To study the effect of the repair of rabbit articular cartilage defects by the composite of chondrogenic induction of autologous MSCs and autologous “two-phase” bone matrix gelatin (BMG). Methods Twentyfour healthy adult New Zealand rabbits weighing 2 to 3 kg were divided into group A, B and C with 8 in each. Autologous MSCsderived from group A were cultured in vitro and observed under inverted phase contrast microscope when enough cells through trypsinization transferring in vitro were obtained. Then the growth curves of 1, 3 and 5 passage culture of MSCs were drawn. The 3rd passage MSCs were induced into chondrogenic differentiation by adding TGF-β1 (10 ng/mL), IGF-1 (10 ng/mL) and vitamin C (50 ng/mL) in vitro. At 8 days after induction, the features of chondrocytes were observed under inverted phase contrast microscope, and immunohistochemical staining and Mallory staining were made. Getting out part of the il ium of group A and B, according to the method of Urist, the “two-phase” BMG was acquired. Chondrogenic induction of autologous MSCs was inoculated into the corresponding BMG to set up a composite of cell-carrier, and then it was observed through scanning electric microscope after 3 days of culture. The model of articular cartilage defects of rabbits was made: in group A, autologous cell-carriers were implanted; in group B, there only existed autologous BMG; in group C, there was nothing. At 8, 12 weeks after operation, the gross, HE staining and immunohistochemical staining were made, and grading scales were evaluated according to Wakitani histological grading method. Results Features of MSCs were as follows: the shape of primary cells was shotspindled and of passage cells was long. As to the growth curves of 1, 3 and 5 passage culture of MSCs, passage cells grew slowly for 3 days after being passaged and went into log-growth during the 3rd and the 7th days and into plateau later, but the 3rd passage cells grew best. Observation of MSCs after chondrogenic induction was performed: the shape of cells was ell iptical and the effect of induction was verified by the positive results of collagen type II, S-100 and Mallory staining. Under scanning electricmicroscope, the structure of BMG was good and cells were observed growing in it well. As far as repair of articular cartilage defects are concerned at 8, 12 weeks after transplantation, the defects in group A were repaired by the hyl ine-l ike tissue and the structures of the cartilage surface and normal cartilage were in integrity, and immunohistochemical staining of collagen type II was positive, while those in group B and C were repaired by the fibrous-l ike tissues and the surfaces were irregular. In Wakitanni histological score, at 8 weeks after operation, group A was (3.50 ± 1.51) points, group B was (10.00 ± 1.41) points and group C was (12.00 ± 0.93) points; at 12 weeks, group A was (1.13 ± 0.99) points, group B was (8.38±1.30) points, and group C was (10.13 ± 1.64) points. At different time points, group A was significantly better than group B and C, showing significant differences (P lt; 0.05). Conclusion Induced autologous MSCs and the composite with autologous “two-phase” BMG have the function to repair articular cartilage defects, and they are better than autologous BMG transplanted only or nothing transplanted.