Objective To evaluate the biocompatibility and safety of a novel orthopedics materials-graded zirconia(ZrO2)hydroxyapatite(HA) composite biomaterials. Methods First, ultrafine powers of ZrO2 and HA powder were prepared by chemical precipitation method, then graded ZrO2-HA composite was synthesized by dry-laying and sintering method. After the physiological saline and culture medium extracts of the composite were prepared, four experiments were conducted as follows:① The mouse acute toxic test consists of 2 groups(n=10). The extracts were intravenously injected to mice in the first group, and physiological saline to mice in the second group. The dose was 50 g/kg. Their toxicity manifestation, morality and the change of weight were recorded.② The standard curve of proliferation and metabolism of L929 cells was established. ③ The cytotoxinic test consists of 3 groups: materials group (extracts of the materials), positive control group (culture fluid with 0.64% phenol), and negative control group (RPMI-1640 culture fluid). Each of three was cultured with cell suspension, and then the morphology of the cells was observed, the relative proliferation rate (RGR) was calculated, and the toxicity was classified. ④ In vitrohemolytic test was divided into 3 groups: extracts, sterile distilled water (positive control) and 0.9% physiological saline. In each of three, 0.2 ml anticoagulant diluted fresh rabbit blood was added. The percentage of hemolysis was tested. ⑤ The muscle and implantation test were divided into 4 groups(n=3). The composite biomaterials were implanted into pygal muscleson either side and lateral condyles of femurs. After surgery, the rats of four groups were sacrificed at 12 and 24 weeks respectively.Tissue slice and scanning electronic microscopy were performed. Results General acute toxic test: no mouse died within 3 weeks; no toxicity symptom or adverse effects were shown within 3 days. The weight of materials group increased by 3.57±0.49 g, and the control group by 3.62±0.61 g, showing no statistically significant difference（Ρgt;0.05）.The standard curve of L929 cell perliferation and metabolism showed that their existed a positive correlation between the number of L929 cells and the perliferation. ③ Cytotoxinic test: cytosomes in the positive control group diminished and appeared round, there were pyknotic nucleus, the attached cells agglomerated; the toxicity was level Ⅳ. The morphology of cells in materials groupand negative control group was normal, and the number of them increased; the toxicity was level Ⅰand level 0, respectively. The MTT color experiments showed that positive control group was significantly lower than materials group and negative control group, showing statistically significant difference (Plt;0.01); there was no statistically significant difference between materials group and negative group.④ Hemolytic test: in vitrohemolytic rate of negative control group was0, of positive control group was 100%, and of materials group was 1.66%, which accords with the standard that hemolytic rate should be lower than 5% specified in ISO. ⑤ Implant test:No apparent rejection reaction took place after the composite was implanted; the composite bonded with the bones of the receptors firmly, which had good bonedinduced effect. Conclusion Graded ZrO2-HA composite bioceramic has good biocompatibility and is suitable for orthopedic biomaterials.
Objective To explore the method of preparing the electrospinning of synthesized triblock copolymers of ε-caprolactone and L-lactide (PCLA) for the biodegradable vascular tissue engineering scaffold and to investigateits biocompatibil ity in vitro. Methods The biodegradable vascular tissue engineering scaffold was made by the electrospinning process of PCLA. A series of biocompatibil ity tests were performed. Cytotoxicity test: the L929 cells were cultured in 96-wellflat-bottomed plates with extraction media of PCLA in the experimental group and with the complete DMEM in control group, and MTT method was used to detect absorbance (A) value (570 nm) every day after culture. Acute general toxicity test: the extraction media and sal ine were injected into the mice’s abdominal cavity of experimental and control groups, respectively, and the toxicity effects on the mice were observed within 72 hours. Hemolysis test: anticoagulated blood of rabbit was added into the extracting solution, sal ine, and distilled water in 3 groups, and MTT method was used to detect A value in 3 groups. Cell attachment test: the L929 cells were seeded on the PCLA material and scanning electron microscope (SEM) observation was performed 4 hours and 3 days after culture. Subcutaneous implantation test: the PCLA material was implanted subcutaneously in rats and the histology observation was performed at 1 and 8 weeks. Results Scaffolds had the characteristics of white color, uniform texture, good elasticity, and tenacity. The SEM showed that the PCLA ultrafine fibers had a smooth surface and proper porosity; the fiber diameter was 1-5 μm and the pore diameter was in the range of 10-30 μm. MTT detection suggested that there was no significant difference in A value among 3 groups every day after culturing (P gt; 0.05). The mice in 2 groups were in good physical condition and had no respiratory depression, paralysis, convulsion, and death. The hemolysis rate was 1.18% and was lower than the normal level (5%). The SEM showed a large number of attached L929 cells were visible on the surface of the PCLA material at 4 hours after implantation and the cells grew well after 3 days. The PCLA material was infiltrated by the inflammatory cells after 1 week. The inflammatory cells reduced significantly and the fiber began abruption after 8 weeks. Conclusion The biodegradable vascular tissue engineering scaffold material made by the electrospinning process of PCLA has good microstructure without cytotoxicity and has good biocompatibil ity. It can be used as an ideal scaffold for vascular tissue engineering.
Objective To evaluate the biocompatibility of a new bone matrix material (NBM) composed of both organic and inorganic materials for bone tissue engineering. Methods Osteoblasts combined with NBM in vitro were cultured. The morphological characteristics was observed; cell proliferation, protein content and basic alkaline phosphatase(ALP) activity were measured. NBM combined with osteoblasts were implanted into the skeletal muscles of rabbits and the osteogenic potential of NBM was evaluated through contraat microscope, scanning electromicroscope and histological examination. In vitro osteoblasts could attach and proliferate well in the NBM, secreting lots of extracellular matrix; NBM did not cause the inhibition of proliferation and ALP activity of osteoblasts. While in vivo experiment of the NBM with osteoblasts showed that a large number of lymphacytes and phagocytes invading into the inner of the material in the rabbit skeletalmuscle were seen after 4 weeks of implantation and that no new bone formation was observed after 8 weeks. Conclusion This biocompat ibility difference between in vitro and in vivo may be due to the immunogenity of NBM which causes cellular immuno reaction so as to destroy the osteogenic environment. The immunoreaction between the host and the organic-inorganic composite materials in tissue engineering should be paid more attention to.
Objective To investigate the biocompatibility of acellular urinary bladder submucosa (AUBS). Methods The acellular collagen matrix of human urinary bladder submucosa was developed using freeze-thawed enzymatic treatment and freeze-drying technique. Human oral keratinocytes were cultured and seeded on AUBS at a density of 2×106/ml in vitro.The proliferation of the cells were observed. Pockets were created in the abdominal muscle wall of 18 SD rats. AUBS in size 1 cm×1 cm was implanted into the pocket. The grafts were observed by light microscope 3, 6, 10, 14, 21 and 28 days after operation. Results AUBSmainly consisted of collagen fibers with a three-dimensional network structure. After the oral keratinocytes were seeded, continous oral epithelium layer was formed on the surface of AUBS after 10 days in vitro. Histological observation of the grafted AUBS showed progressive cell infiltration at 6 days. New capillaries formed at 14 days. The collagen fibers arranged regularly at 28 days after implantation. Conclusion Freeze-dried AUBS may be used as a suitable scaffold for tissue regeneration, which can induce cell proliferation both in vivo and in vitro and has good biocompatibilty.
Objective To investigate the influence of different dose levels of hydroxyapatite/tricalcium phosphate (HA/TCP) on the proliferation and alkalinephosphatase (ALP) activity of rabbit osteoblasts. Methods Three different doselevels of HA/TCP (10%, 40%, 70%) were co-cultivated with rabbit osteoblasts respectively. The proliferation and ALP expression capacity of osteoblasts were examined with MTT method and enzyme histochemistry once every 24 hours until 5 days. Three control groups of other materials were treated and examined in the sameway: rabbit osteoblasts as normal control; polyvinylchloride as positive control; titanium alloy as negative control. Results There was remarkable timeeffect relationship in the proliferation of osteoblasts. Ten percent HA/TCP did not affect osteoblasts growth while 40% HA/TCP could slow the cell growth rate down though time-effect relationship still existed. The proliferation of osteoblasts stagnated when co-cultivated with 70% HA/TCP. On the other hand, 10% HA/TCP could cause reversible damage on ALP activity of osteoblasts, whereas when the dose was40%, and the cultivation lasted 6 days the damage was irreversible. Three different dose levels of titanium alloy (10%, 40%, 70%) had no effect on the proliferation or ALP activity of osteoblasts. Conclusion Dosage is an important factor affecting the biocompatibility evaluation of biomaterial. It suggests that dose choosing should be more specified upon each individual biomaterial. It also indicates that ALP may be a good supplementary index of the cell compatibility of material.
This paper is to evaluate the biocompatibility and cytotoxicity of a new Ni-free Zr-based bulk metallic glass (BMG), Zr60.14Cu22.31Fe4.85Al9.7Ag3, by comparing it with conventional Ti6Al4V alloy. According to ISO 10993-5:1999 and GB/T 16886.5-1997 standards, Zr60.14Cu22.31Fe4.85Al9.7Ag3, pure Zr and Ti6Al4V materials were extracted with surface area of sample/volume of medium ratio being 1 cm2/mL and 0.5 cm2/mL, respectively. The viabilities of MG-63 cells (Human osteosarcoma cell line) cultured in the BMG medium extracts for 1, 3 and 5 days were determined by CCK-8 assay. The cellular morphology of MG-63 cells cultured on the surface of samples for 3 days was tested through laser scanning confocal microscopy (LSCM) and scanning electron microscopy (SEM). The relative growth rate (RGR) of MG-63 cells cultured in Zr60.14Cu22.31 Fe4.85 Al9.7Ag3 and pure Zr were both more than 85%, indicating that the cytotoxicity of BMG was relatively low and met the national biomedical material eligibility standard. There was insignificant difference in the morphology of MG-63 cells cultured in the BMG medium extracts and the control group through LSCM and SEM, which showed the BMG had excellent biological compatibility. The Zr-based bulk metallic glass Zr60.14Cu22.31Fe4.85Al9.7Ag3 and the conventional Ti6Al4V alloy both had no obvious cytotoxicity to MG-63 cells. These results provided evidence that the new Zr-based bulk metallic glass could be potential replacement material for the orthopedic surgical implant.
OBJECTIVE To study the biocompatibility on bioactive glass ceramics (BGC) and polylactic acid (PLA) combined with cultured bone marrow stromal cells (BMSCs) in bone tissue engineering. METHODS BMSCs were cultured combined with BGC and PLA in vitro, and the morphological characters, cell proliferation, protein content, and alkaline phosphatase activity were detected. RESULTS: BMSCs could be attached to and extended on both BGC and PLA, and normally grown, proliferated, had active function. BGC could promote cell proliferation. CONCLUSION The results show that both BGC and PLA have good biocompatibility with BMSCs, they can be used as biomaterials for cell transplantation in tissue engineering.
Objective To investigate the biocompatibil ity of silk fibroin nanofibers scaffold with olfactory ensheathing cells (OECs) and to provide an ideal tissue engineered scaffold for the repair of spinal cord injury (SCI). Methods Silk fibroin nanofibers were prepared using electrospinning techniques and were observed by scanning electron microscope (SEM). Freshly isolated OECs from SD rats purified by the modified differential adherent velocity method were cultured. The cells at passage 1 (1 × 104 cells/cm2) were seeded on the poly-l-lysine (control group) and the silk fibroin nanofibers (experimental group) coated coversl ips in Petri dish. At desired time points, the morphological features, growth,and adhesion of the cells were observed using phase contrast inverted microscopy. The OECs were identified by the nerve growth factor receptor p75 (NGFR p75) immunofluorescence staining. The viabil ity of OECs was examined by l ive/dead assay. The prol iferation of OECs was examined by MTT assay. The cytotoxicity of the nanofibers was evaluated. Results The SEM micrographs showed that the nanofibers had a smooth surface with sol id voids among the fibers, interconnecting a porous network, constituted a fibriform three dimensional structure and the average diameter of the fibers was about (260 ± 84) nm. The morphology of OECs on the experimental group was similar to the cell morphology on the control group, the cells distributed along the fibers, and the directions of the cell protrusions were in the same as that of the fibers. Fluorescence microscopy showed that the purity of OECs was 74.21% ± 2.48% in the experimental group and 79.05% ± 2.52% in the control group 5 days after culture. There was no significant difference on cell purity between two groups (P gt; 0.05). The OECs in the experimental group stained positive for NGFR p75 compared to the control group, indicating that the cells in the experimental group still maintained the OECs characteristic phenotype. Live/dead staining showed that high viabil ity was observed in both groups 3 days after culture. There was no significant difference on cell viabil ity between two groups. The prol iferation activity at 1, 3, 5, 7, and 10 days was examined by MTT assay. The absorbency values of the control group and the experimental group had significant differences 3 and 5 days after culture (P lt; 0.05). The relative growth rates were 95.11%, 90.35%, 92.63%, 94.12%, and 94.81%. The cytotoxicity of the material was grade 1 and nonvenomous according to GB/T 16886 standard. Conclusion Silk fibroin nanofibers scaffold has good compatibility with OECs and is a promising tissue engineered scaffold for the repair of SCI.
Objective To investigate the biocompatibility of diamond-like carbon(DLC) coated NickelTitanium shape memory alloy with osteoblasts cultured invitro. Methods Rabbit’s osteoblasts were incubated with DLCcoated NickelTitanium shape memory alloy disks and uncoated ones of equal size for 5 days. The control group（without shape memory alloy in culture media） was performed simultaneously. The cultured cells were counted and graphed. The samples from culture media were collected and the concentrations of alkaline phosphatase (ALP) and nickel（Ni2+） were measured from the 1st to 5th day respectively. Results The proliferation of osteoblasts and the concentration of ALP in both DLC-coated group and control gruop was higher than uncoated group. The proliferation of osteoblasts on the 3rd, 4th, and 5th day in both DLC-coatedgroup and control group was significantly higher than that in the uncoated group(P＜0.05). The concentration of ALP in DLC-coated group on the 2nd, 3rd, and 5th day and in the control group on the 3rd, 4th, and 5th day was significantly higher than that in the uncoated group(P＜0.05). The concentration of Ni2+ on the 3rd, 4th, and 5th day was significantly lower than that in the uncoated group(P＜0.05). Conclusion DLC- coated NickelTitanium shape memory alloys appears to have better biocompatibility with osteoblast cultured in vitro compared to uncoated ones.
Objective To investigate the biocompatibility of true bone ceramic (TBC) and provide experimental basis for clinic application. Methods TBC was prepared from healthy adult bovine cancellous bone by deproteinization and high temperature calcinations. Mouse fibroblast cell line (L929 cells) were cultured with the leaching liquor of TBC in vitro, and the cytotoxicity was evaluated at 2nd, 4th, and 7th days. L929 cells were inoculated into the TBC and cultured for 4 days. The cell adhesion and proliferation on the surface of the TBC were observed by scanning electron microscopy, and evaluated the cell compatibility of TBC. Ten New Zealand white rabbits were divided into 2 groups, and drilled holes at the tibia of both hind limbs. TBC and hydroxyapatite (HA) were implanted into the left side (experimental group) and the right side (control group), respectively. And the biocompatibility of TBC was evaluated by general observation and histological observation at 4 and 26 weeks after implantation. Results Cytotoxicity test showed that the cytotoxicity level of leaching liquor of TBC was grade 0-1. Cell compatibility experiments showed that the L929 cells adhered well on the surface of TBC and migrated into the pores. The implantation test in vivo showed that experimental group and control group both had mild or moderate inflammatory response at 4 weeks, and new bone formation occurred. At 26 weeks, there was no inflammatory reaction observed in both groups, and new bone formation was observed in varying degrees. Conclusion TBC have good biocompatibility and can be used to repair bone defect in clinic.